Corroseal® Technical Data
Product Description
Corroseal® is a water based rust converter combined with a non pigmented high quality latex metal primer. The converter segments turn rust into a barrier layer of black non rusting magnetite. The metal primer acts as a bonding agent for oil-based intermediate and finish coatings of epoxy, enamel, acrylic, polyurethane and moisture-cured urethane, and with water based coatings not subject to tannin staining. Water based coatings may require an oil based stain blocker as an intermediate application. Corroseal® is non flammable and non corrosive.
Basic Use
Corroseal® is recommended for use on rusted or partially rusted steel surfaces as a rust converter / metal primer, and as an etch primer on aged tight paint of any color, and as a sealer on non ferrous metals such as some aluminum, copper, and brass.
Availability SKU# 82320 - 1 quart jug
SKU# 82331 - 1 gallon jug
SKU# 82335 - 5 gallon pail
SKU# 82320 - 52 gallon drum
Appearance Milky, off-white to tan liquid
Odor Very mild
Thinning Do not thin
Coverage 200 square feet per gallon @ 2.5 mil dry film thickness. 4.9 square meters per liter.
Spreading Rate 8-10 mils wet film thickness, 200-250 microns, to create optimum dry film thickness of 2.5 mils to 3.5 mils DFT (65 to 90 microns) to cover anchor profile
Cleanup Soap and water for equipment, hands, and clothes. Clean dried spatter with lacquer thinner.
Physical Properties
VOC (ATSM D 3960) 60 grams per Liter, 8 oz per gallon
Non volatiles by volume 31%
Non volatiles by weight 35%
Weight per gallon 8.6 lbs, 3.91 Kg
pH 3.0
Flash point (Closed Cup ASTM D 56) >200°F, > 93°C
Viscosity (Brookfield model LVF #2 spindle, 60 rpm) 300 cps
Heat Resistance Resists heat aging up to 270°F. Useful properties up to 350°F.
UV Resistance (ASTM G-23 Ultraviolet Testing) 1000 hours - No Fading
Cathodic Disbondment Corroseal Primer to rusted steel and top coated with - ASTM D4541 Wasser MoistureCure-CR-PW Average Pull Force at Failure 1128 psi
Shelf life (ASTM D 1849) resists greater than 1 week at 140°F and up to or over one year between 38°F and 105°F, 3°C and 41°C. Avoid continuous direct sunlight. KEEP FROM FREEZING. Discard after freezing.
Dry time (ASTM D 1640) at 3 mils wet film, 76 microns.
Set to touch - 3 minutes
Cotton free - 10 minutes
Dry to touch - 30 minutes
Hard dry - 40 minutes
Through fingernail hard - 60 minutes
Rejects rainwater at 77°F, 25°C - No wash off 240 minutes
Recoat time at 77°F, 25°C Brush / Roller 15-30 minutes, Spray 10-20 minutes or between set to touch and dry to touch (tacky).
Top coat time 24 hours minimum, up to 30 days
Technical Services
Technical advice is available by calling Corroseal® at 1-800-237-1573 or email inquiries to [email protected]. Visit www.corroseal.com for more information. Made in the USA by Rodda Paint Company, Portland Oregon.
Product Description
Corroseal® is a water based rust converter combined with a non pigmented high quality latex metal primer. The converter segments turn rust into a barrier layer of black non rusting magnetite. The metal primer acts as a bonding agent for oil-based intermediate and finish coatings of epoxy, enamel, acrylic, polyurethane and moisture-cured urethane, and with water based coatings not subject to tannin staining. Water based coatings may require an oil based stain blocker as an intermediate application. Corroseal® is non flammable and non corrosive.
Basic Use
Corroseal® is recommended for use on rusted or partially rusted steel surfaces as a rust converter / metal primer, and as an etch primer on aged tight paint of any color, and as a sealer on non ferrous metals such as some aluminum, copper, and brass.
- Protects against future rusting
- Can be used on welds
- Eliminates need to mechanically blast to white metal in many instances
- Not recommended for outside hull underwater applications
Availability SKU# 82320 - 1 quart jug
SKU# 82331 - 1 gallon jug
SKU# 82335 - 5 gallon pail
SKU# 82320 - 52 gallon drum
Appearance Milky, off-white to tan liquid
Odor Very mild
Thinning Do not thin
Coverage 200 square feet per gallon @ 2.5 mil dry film thickness. 4.9 square meters per liter.
Spreading Rate 8-10 mils wet film thickness, 200-250 microns, to create optimum dry film thickness of 2.5 mils to 3.5 mils DFT (65 to 90 microns) to cover anchor profile
Cleanup Soap and water for equipment, hands, and clothes. Clean dried spatter with lacquer thinner.
Physical Properties
VOC (ATSM D 3960) 60 grams per Liter, 8 oz per gallon
Non volatiles by volume 31%
Non volatiles by weight 35%
Weight per gallon 8.6 lbs, 3.91 Kg
pH 3.0
Flash point (Closed Cup ASTM D 56) >200°F, > 93°C
Viscosity (Brookfield model LVF #2 spindle, 60 rpm) 300 cps
Heat Resistance Resists heat aging up to 270°F. Useful properties up to 350°F.
UV Resistance (ASTM G-23 Ultraviolet Testing) 1000 hours - No Fading
Cathodic Disbondment Corroseal Primer to rusted steel and top coated with - ASTM D4541 Wasser MoistureCure-CR-PW Average Pull Force at Failure 1128 psi
Shelf life (ASTM D 1849) resists greater than 1 week at 140°F and up to or over one year between 38°F and 105°F, 3°C and 41°C. Avoid continuous direct sunlight. KEEP FROM FREEZING. Discard after freezing.
Dry time (ASTM D 1640) at 3 mils wet film, 76 microns.
Set to touch - 3 minutes
Cotton free - 10 minutes
Dry to touch - 30 minutes
Hard dry - 40 minutes
Through fingernail hard - 60 minutes
Rejects rainwater at 77°F, 25°C - No wash off 240 minutes
Recoat time at 77°F, 25°C Brush / Roller 15-30 minutes, Spray 10-20 minutes or between set to touch and dry to touch (tacky).
Top coat time 24 hours minimum, up to 30 days
Technical Services
Technical advice is available by calling Corroseal® at 1-800-237-1573 or email inquiries to [email protected]. Visit www.corroseal.com for more information. Made in the USA by Rodda Paint Company, Portland Oregon.